Abstract:
Acryli-c based pressure sensitive adhesives (PSA) were synthesized by changing the
monomer combinations and introducing hydroxyethyl acrylate (HEA) as a functional monomer. The
impact of nano-fillers on mechanical properties of the said adhesive was analyzed by incorporating
different dosages of modified and unmodified grades of montmorillonite. Monomer mixture of nbutylacrylate
(BA), 2-ethylhexyl acrylate (2-EHA), Hydroxyethyl acrylate (HEA) and Methacrylic
acid (MAA) monomer mixtures were used to disperse the nano-clay. Mechanical blending technique
was used to disperse the nano-clay with the synthesized adhesives.
Adhesive synthesized using the combination of BAl2EHA exhibit remarkable improved properties for
tack and peel strength. However, shear strength of synthesized adhesives was not up to the standard
level. Adhesion performance of water based PSAs mainly depend on monomer composition.
Percentage of HEA present in the adhesive was increased and the shear strength of the adhesive
samples increases accordingly.
When we consider the shear strength of the adhesive series having nano-clay, all the adhesives
displayed better improvement of shear strength with the increase of MMT and OMMT percentages.
However, tack and peel values have gradually decreased. Adhesive with MMT showed better shear
strength compared to adhesives containing OMMT as a nano-filler. The optimized adhesion properties
were obtained in the range of 0.1 to 0.25% composition of nano-clay. At this range all three properties
(peel, shear and tack) of the adhesive were well balanced.
IR data confirm the desired synthetic products. Tg values obtained from DSC thermo grams are in the
range of -48°C to -55 °c and therefore all the adhesives are soft polymers. Generally, soft polymers
are highly tacky in nature, when it is elastic and flexible. All the adhesive samples have only one Tg
which indicate that all the adhesives are random copolymers.